Effect Of Annealing Process On Mechanical Properties Of N6 Nickel Plate

2024-01-05 18:00:06

(1) As the temperature increases, the elongation of the sheet after N6 Nick Plate cold rolling increases first and then decreases, reaching a maximum at 500 ° C.

Nick Plate

(2) After annealing at 350 ° C, a large number of unevenly distributed fine particles appeared between the grains that were originally deformed, and as the temperature increased to 450 ° C, there were obvious precipitated phases, and at the same time, impurity element aggregation occurred. When the recrystallization at ℃ was completed, it was equiaxed and the grain deformation caused by rolling had disappeared.


(3) N6 pure nickel is annealed at 500 ℃ × 1 h after cold rolling, the work hardening phenomenon of the plate is eliminated, and the comprehensive mechanical properties reach the best.


YOU MAY LIKE

Molybdenum Bolt

Molybdenum Bolt

View More
Molybdenum Spot Welding Head

Molybdenum Spot Welding Head

View More
pure niobium sheet

pure niobium sheet

View More
black tungsten wire

black tungsten wire

View More
expansion alloy

expansion alloy

View More
thin nickel foil

thin nickel foil

View More