A Preparation Method For Weld Nickel Alloys Electrodes

2024-01-05 18:00:06

    weld nickel alloys electrodes can produce arc under a small current and keep to work under a small current.It also works well under a low direct current.It is better for welding pipeline and thin and small parts,welding continuosly,welding for a special number parts.


      What does weld nickel alloys electrodes welding method look like?

      A preparation method for weld nickel alloys electrodes

    The preparation method of the weld nickel alloys electrodes further includes the following steps: pre-treatment of the prepared nickel conductor electrode is performed by acidic electroless nickel plating or alkaline electroles nickel plating;

 

        Wherein, the method includes the following steps:

       1、Ni, boron, aluminum, zinc powder is mixed according to a predetermined ratio, the mixture is pressed at a pressure of 6. 0-9. 0 tons / cm2, the pressure of the knot will be obtained in 2. 40-3 33Pa vacuum environment, 1200-1300 °C temperature in the heat 8-10 hours, after cooling the crushing block to 80-120nm, obtained nickel alloy powder;

      2. The nickel alloy powder, the glass powder, the ethyl cellulose, and the terpineol binder are mixed in a predetermined ratio to obtain a nickel slurry, wherein the glass powder is made of MgO, CaO, A1203, Si02, B203, PbO. Made by crushing after melting;

  The prepared nickel paste was printed on an alumina substrate and dried, and finally sintered in air to obtain a nickel conductor electrode.

 weld nickel alloys electrodes.jpg

     3, wherein, the predetermined proportion of the nickel, boron, aluminum, zinc powder mixture: by weight percentage, boron powder 1. 〇_8. 0,0. 1-1. 0, zinc powder 0. 3-3 . 0 Peaceful measure of silver powder, the sum of the components is 100%.

The sintering temperature is 850-1000°C.

The particle size of nickel powder is < 30 μm.

      The predetermined proportions of nickel alloy powder, glass powder, ethyl cellulose and terpineol binder are as follows: nickel alloy powder 70-80, glass powder 5-10, ethyl cellulose and terpineol, in percent by weight. Adhesive 10-25.

 

       The glass powder was made by melting MgO, CaO, A1203, Si02, B203, PbO and then pulverized into concrete: 2-5% Mg0, 3-5% Ca0, 5-10% A1203 in percentage by weight. 10-23% of SiO2, 13-20% of B20 3, and 37-67% of PbO were mixed and melted at a temperature of 1300C to obtain a glass frit;



        If your industry needs to buy high quality  weld nickel alloys electrodes, please contact us!

        EMAIL:rmd1994@yeah.net.



YOU MAY LIKE

Tungsten Wire

Tungsten Wire

View More
Titanium Bolts

Titanium Bolts

View More
tungsten filament wire

tungsten filament wire

View More
Tungsten crucible

Tungsten crucible

View More
Molybdenum wire for EDM

Molybdenum wire for EDM

View More
Molybdenum Wire

Molybdenum Wire

View More